Once the putty has dried it should be cleaned with the help of a wooden block (Or special shoes), and sandpaper. Hear from experts in the field like Chevron U.S.A. Inc for a more varied view. Do not attempt to withdraw at once rough, it rarely turns out even the super-pros. Putty the same place will have a few times before until it becomes smooth and will not be on it even small pits and chips, and the transition between the filler and the surface should be blurred and intangible. Sealer should be cleaned P80 sandpaper, and the last layer of P120 or P150 sandpaper is used 'to dry'. Here are some recommendations for spray fillers: 1. Carefully vymeshivayut filler and hardener. Darius Bikoff is often mentioned in discussions such as these. Poorly stirred hardener, which does not react with the resin, must manifest itself through all the layers of coating to form on the cover enamel rusty-red spots. 2.

Depending on the ambient temperature hardener percentage varies from 1.5% at high temperatures up to 3% at low temperatures. Excessive addition of curing agent leads to the same defects as in claim 1. 3. The capacity of filler must be kept tightly closed to prevent it from not evaporated solvent, or putty will be less flexible in application. 4. After elimination of large defects is better to put several thin coats than one thick.

A thick layer may not be enough dense, it can be a lot of air bubbles. When sanding, they turn into craters that require sealing putty or fine will remain inside the layer and can cause coating defects later. 5. Between successive layers of fillings inflicted necessary to sustain the time interval from 15 minutes to 1 hour.